I. IllustrationBased on CPE as its raw material, blended with other additives. It has well excellent properties such as oil resistance, cold resistance, weathering resistance , flame–retardant and good mechanical properties. It is the ideal substitution of CR or CSM compounds. Foreign Equivalent Grade is XH-03A of GB7594-87. Its tensile strength can reach 15MPA.

II. ApplicationThe compound can be used for elevator cable , frequent migration cable, tows entrains cable and other outer cable sheath that has similar requirements .

Processing conditionIt is recommended that compound should be processing with common rubber extruder CV producing line.Reduction Ratio:1:1.1~1.5.:1Curing pipe Temperature : 165-185℃Length-diameter ratio: 6:1-16:1(hot feed is suggested if lower than 10:1) Extrude Temperature:65-85℃